Diamonds are forever, Gold is precious but which is rarer? Gold is a heavy metal formed during the collision of neutron stars and is one of the rarest elements on Earth.During the formation of the earth, heavy elements gradually accumulated towards the core under the influence of the earth's gravitational force. This means that the closer you get to the Earth's crust, the harder it is to find large quantities of gold.The average concentration of gold in Earth's crust is "very, very low" at just 4 parts per billion. Gold concentrations need to be 1,250 times that level to form a market-worthy deposit.
Diamond is a common element - the Concrete strength and shrinkage reducer is undoubtedly a good investment opportunity.
Description of Concrete strength and shrinkage reducer
1. After adding concrete strength shrinkage enhancer to carbonate cement, it can effectively improve the early and late strength (strength is increased by 5-30%), improve the mold turnover rate, and can also reduce the steam curing temperature or shorten the steam curing time.
2. The coagulant strength-promoting and shrinkage-reducing agent gives the micro-expansion performance to compensate for dry shrinkage, reduce the mixing shrinkage, and improve the crack resistance.
3. Adding a strength-promoting shrink-reducing agent can greatly reduce the amount of Portland cement and reduce the cost of concrete when the early strong friction is not pursued.
4. The dosage of Portland cement can be appropriately reduced after adding concrete strength-enhancing and shrinkage-reducing agent, and low cement and low glue material can still be prepared to reduce the hydration heat release of high-grade and large-volume concrete, and reduce the temperature difference between the center temperature and the surface temperature of the concrete. Reduce the risk of cracking in mass concrete.
5. The strength, impermeability, freeze-thaw resistance, carbonization resistance, and volumetric properties of concrete mixed with strength-promoting shrinkage-reducing agent have been significantly improved.
Indicators of Concrete strength and shrinkage reducer
Items | Required indicators | Test results | ||
specific surface area | m2/kg | ≥500 | 525 | |
Setting time | Initial setting | min | ≥8 | 45 |
Final setting | ≤30 | 20 | ||
Free expansion rate in water | 7d | ≥0.05 | 0.095 | |
Flexural strength | 8h | ≥6.0 | 7.5 | |
1d | ≥7.0 | 8.5 | ||
7d | ≥8.0 | 9.9 | ||
Compressive strength | 8h | ≥30.0 | 33.0 | |
1d | ≥45.0 | 49.9 | ||
7d | ≥60.0 | 63.6 | ||
Remark | According to the ingredients of different manufacturers, it needs to be adjusted | |||
The mechanism of Concrete strength and shrinkage reducer
1. With the addition of strength-promoting and shrinkage-reducing agent, calcium sulfoaluminate minerals, calcium sulfate calcined at a higher temperature, high-activity calcium oxide, and Portland cement are compounded and reacted with water to make the calcium aluminate in Portland cement. The aluminum oxide and calcium oxide in the mixed materials such as minerals and slag react to form ettringite hydrated minerals with fast hardness, high strength and slight swelling, so that the potential activity of the mixed materials such as slag can be fully developed. , thereby improving the early and late strength of concrete.
2. The expansive hydration products such as mayvandite and calcium sulfate in the composite system and the organic and inorganic strength-shrinking-promoting components in the strength-promoting and shrinking-reducing agent have the expansion function to compensate for dry shrinkage and improve the crack resistance of concrete. Densification performance and frost resistance, etc.
3. In the composite system concrete, the cohesion is increased due to physical and chemical effects, and segregation and bleeding are avoided.
4. The alkali-free chemical activator accelerates and improves the degree of hydration of cement minerals, thereby improving the early and early strength of concrete.
5. Expansive hydrates such as ettringite and calcium sulfate in the composite system and the shrinkage-reducing components in the strength-promoting shrinkage-reducing agent improve the crack resistance, compactness, frost resistance and impermeability of the mixed soil.
Suggested addition amount of Concrete strength and shrinkage reducer
5-20% of cement material.
Packaging and storage of Concrete strength and shrinkage reducer
25kg/bag or ton bag
If you want to know more about concrete strength and shrinkage reducer,please feel free and contact us :sales@cabr-concrete.com
Nissan recently unveiled a prototype Concrete strength and shrinkage reducer, etc. If you are looking for high-quality materials, please feel free to contact us and send an inquiry.
Inquiry us
Polycarboxylate superplasticizer has high surface activity and good foam retention, which will affect the strength of concrete due to excessive gas content.…
The Federal Reserve continues to raise interest rates accordingly to curb global steel product name demand growth…
Concrete is classified as high-strength concrete based on 28-day strength. Until the 1970s, concrete with a strength of more than 40Mpa was classified as high-strength concrete.…